Wood imitation polyurethane systems are easy to process because of the hard and long processing of wood products in furniture and decor area. 2-component wood imitation polyurethane systems (polyol / isocyanate), high strength, hardness, screwability and fast processability features are in the foreground.
| SYSTEM |
SYSTEM DESCRIPTION |
| A |
TEKimpol 001 |
Polyol Mixture |
| B |
TEKimnat 001 |
Diphenylmethane Diisocyanate |
IMPLEMENTATION
2-component system for hard foam production
STORAGE AND PREPARATION
Polyurethane systems are sensitive to moisture. Covers should be stored in enclosed barrels at the storage temperatures given in component properties.
Shelf life is valid for products stored under suitable storage temperature and conditions.
A must be homogenized by mixing before use.
COMPONENT FEATURES
|
UNIT |
A |
B |
METHOD |
| Storage Temperatures |
°C |
18-25 |
18-25 |
|
| Shelf life |
Ay |
6 |
6 |
|
| Specific Weight |
g/cm³ |
0,97 |
1,12 |
ASTM D891 |
| Viscosity (25°C) |
mPa.s |
130±30 |
195±30 |
DIN 53019 |
| Free NCO content |
% |
– |
20,5-21,5 |
ASTM D 2572 |
WORKING CONDITIONS
|
UNIT |
A |
B |
METHOD |
| Tank Temperatures |
°C |
25-30 |
25-30 |
|
| Recommended Mold Temperatures |
°C |
30-45 |
|
|
REACTION PROFILE
| MIXING RATIO (A/B) |
UNIT |
100 |
METHOD |
| polyol |
wEİGHT |
EFKimpol 001 100 unit |
|
| Isocyanate |
Weight |
EFKimnat 001 100 unit |
|
| Non-stick time |
s. |
170±15 |
|
| Free Density |
kg/m³ |
980±50 |
|
* The values given in the reaction profile are the values obtained with the mechanical mixer rotating at 5000 rpm in the laboratory.
All information provided in this document is based on our knowledge and experience currently available to us. However; external conditions and application factors that may affect the application and process of our product are beyond our control. Therefore, our company cannot be held responsible for any errors or damages that may occur in the product to be produced during or after the application.
We recommend that practitioners use our products for their own control and testing. The data contained herein shall not be construed as guaranteeing any property of the material or its suitability for private use.